The effect of silica nanoparticles on corrosion of steel by molten carbonate eutectic (42.7% Li2CO3, K2CO3) was investigated. The experimental design was based on static coupon immersion … Mehr…
The effect of silica nanoparticles on corrosion of steel by molten carbonate eutectic (42.7% Li2CO3, K2CO3) was investigated. The experimental design was based on static coupon immersion methodology where a coupon (material under study, in this case a rectangular stainless steel specimen of SS304 with dimensions approximately 5X20X.6mm and weight .5gm) is exposed to a static corroding environment for predetermined periods of time. The testing times were 2, 4 and 6 weeks. The temperature during testing was maintained at a constant 520C. The instantaneous corrosion rates were determined by normalizing the mass loss with respect to time and area. The mass loss was determined by descaling the corroded steel coupons using concentrated hydrochloric acid. The instantaneous corrosion rates obtained from all three times showed a reduction in corrosion of steel by molten carbonate eutectics when doped with silica 1% by weight in comparison to the molten base carbonate eutectics. The results showed that doping the carbonate eutectic with silica nanoparticles (1% by weight) reduced the corrosion of steel by half in comparison to the corrosion without doping. Buch (fremdspr.) Ashwin Padmanaban Iyer Taschenbuch, LAP LAMBERT Academic Publishing, 12.12.2011, LAP LAMBERT Academic Publishing, 2011<
Thalia.at
Nr. 30759074. Versandkosten:, Versandfertig in 7 - 9 Tagen, AT. (EUR 0.00) Details...
(*) Derzeit vergriffen bedeutet, dass dieser Titel momentan auf keiner der angeschlossenen Plattform verfügbar ist.
Paperback, [PU: LAP Lambert Academic Publishing], The effect of silica nanoparticles on corrosion of steel by molten carbonate eutectic (42.7% Li2CO3, K2CO3) was investigated. The experim… Mehr…
Paperback, [PU: LAP Lambert Academic Publishing], The effect of silica nanoparticles on corrosion of steel by molten carbonate eutectic (42.7% Li2CO3, K2CO3) was investigated. The experimental design was based on static coupon immersion methodology where a coupon (material under study, in this case a rectangular stainless steel specimen of SS304 with dimensions approximately 5X20X.6mm and weight .5gm) is exposed to a static corroding environment for predetermined periods of time. The testing times were 2, 4 and 6 weeks. The temperature during testing was maintained at a constant 520C. The instantaneous corrosion rates were determined by normalizing the mass loss with respect to time and area. The mass loss was determined by descaling the corroded steel coupons using concentrated hydrochloric acid. The instantaneous corrosion rates obtained from all three times showed a reduction in corrosion of steel by molten carbonate eutectics when doped with silica 1% by weight in comparison to the molten base carbonate eutectics. The results showed that doping the carbonate eutectic with silica nanoparticles (1% by weight) reduced the corrosion of steel by half in comparison to the corrosion without doping., Electrical Engineering<
[EAN: 9783847304579], Neubuch, [PU: LAP LAMBERT Academic Publishing], TECHNIK WäRMETECHNIK ENERGIETECHNIK KRAFTWERKTECHNIK HOT CORROSION OF STEEL CARBONATE EUTECTICS SILICA NANO-PARTIC… Mehr…
[EAN: 9783847304579], Neubuch, [PU: LAP LAMBERT Academic Publishing], TECHNIK WäRMETECHNIK ENERGIETECHNIK KRAFTWERKTECHNIK HOT CORROSION OF STEEL CARBONATE EUTECTICS SILICA NANO-PARTICLES, Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Padmanaban Iyer AshwinThe author holds a Master\\ s in Mechanical Engineering from Texas A&M University, College Station, Texas. His interests ar, Books<
[ED: Kartoniert / Broschiert], [PU: LAP LAMBERT Academic Publishing], Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Padma… Mehr…
[ED: Kartoniert / Broschiert], [PU: LAP LAMBERT Academic Publishing], Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Padmanaban Iyer AshwinThe author holds a Master s in Mechanical Engineering from Texas A&M University, College Station, Texas. His interests are, DE, [SC: 0.00], Neuware, gewerbliches Angebot, Softcover, 72, [GW: 125g], Auflage, Banküberweisung, PayPal<
booklooker.de
Moluna GmbH Versandkosten:Versandkostenfrei, Versand nach Deutschland. (EUR 0.00) Details...
(*) Derzeit vergriffen bedeutet, dass dieser Titel momentan auf keiner der angeschlossenen Plattform verfügbar ist.
The effect of silica nanoparticles on corrosion of steel by molten carbonate eutectic (42.7% Li2CO3, K2CO3) was investigated. The experimental design was based on static coupon immersion … Mehr…
The effect of silica nanoparticles on corrosion of steel by molten carbonate eutectic (42.7% Li2CO3, K2CO3) was investigated. The experimental design was based on static coupon immersion methodology where a coupon (material under study, in this case a rectangular stainless steel specimen of SS304 with dimensions approximately 5X20X.6mm and weight .5gm) is exposed to a static corroding environment for predetermined periods of time. The testing times were 2, 4 and 6 weeks. The temperature during testing was maintained at a constant 520C. The instantaneous corrosion rates were determined by normalizing the mass loss with respect to time and area. The mass loss was determined by descaling the corroded steel coupons using concentrated hydrochloric acid. The instantaneous corrosion rates obtained from all three times showed a reduction in corrosion of steel by molten carbonate eutectics when doped with silica 1% by weight in comparison to the molten base carbonate eutectics. The results showed that doping the carbonate eutectic with silica nanoparticles (1% by weight) reduced the corrosion of steel by half in comparison to the corrosion without doping. Buch (fremdspr.) Ashwin Padmanaban Iyer Taschenbuch, LAP LAMBERT Academic Publishing, 12.12.2011, LAP LAMBERT Academic Publishing, 2011<
Nr. 30759074. Versandkosten:, Versandfertig in 7 - 9 Tagen, AT. (EUR 0.00)
Paperback, [PU: LAP Lambert Academic Publishing], The effect of silica nanoparticles on corrosion of steel by molten carbonate eutectic (42.7% Li2CO3, K2CO3) was investigated. The experim… Mehr…
Paperback, [PU: LAP Lambert Academic Publishing], The effect of silica nanoparticles on corrosion of steel by molten carbonate eutectic (42.7% Li2CO3, K2CO3) was investigated. The experimental design was based on static coupon immersion methodology where a coupon (material under study, in this case a rectangular stainless steel specimen of SS304 with dimensions approximately 5X20X.6mm and weight .5gm) is exposed to a static corroding environment for predetermined periods of time. The testing times were 2, 4 and 6 weeks. The temperature during testing was maintained at a constant 520C. The instantaneous corrosion rates were determined by normalizing the mass loss with respect to time and area. The mass loss was determined by descaling the corroded steel coupons using concentrated hydrochloric acid. The instantaneous corrosion rates obtained from all three times showed a reduction in corrosion of steel by molten carbonate eutectics when doped with silica 1% by weight in comparison to the molten base carbonate eutectics. The results showed that doping the carbonate eutectic with silica nanoparticles (1% by weight) reduced the corrosion of steel by half in comparison to the corrosion without doping., Electrical Engineering<
[EAN: 9783847304579], Neubuch, [PU: LAP LAMBERT Academic Publishing], TECHNIK WäRMETECHNIK ENERGIETECHNIK KRAFTWERKTECHNIK HOT CORROSION OF STEEL CARBONATE EUTECTICS SILICA NANO-PARTIC… Mehr…
[EAN: 9783847304579], Neubuch, [PU: LAP LAMBERT Academic Publishing], TECHNIK WäRMETECHNIK ENERGIETECHNIK KRAFTWERKTECHNIK HOT CORROSION OF STEEL CARBONATE EUTECTICS SILICA NANO-PARTICLES, Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Padmanaban Iyer AshwinThe author holds a Master\\ s in Mechanical Engineering from Texas A&M University, College Station, Texas. His interests ar, Books<
[ED: Kartoniert / Broschiert], [PU: LAP LAMBERT Academic Publishing], Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Padma… Mehr…
[ED: Kartoniert / Broschiert], [PU: LAP LAMBERT Academic Publishing], Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Padmanaban Iyer AshwinThe author holds a Master s in Mechanical Engineering from Texas A&M University, College Station, Texas. His interests are, DE, [SC: 0.00], Neuware, gewerbliches Angebot, Softcover, 72, [GW: 125g], Auflage, Banküberweisung, PayPal<
Versandkosten:Versandkostenfrei, Versand nach Deutschland. (EUR 0.00) Moluna GmbH
1Da einige Plattformen keine Versandkonditionen übermitteln und diese vom Lieferland, dem Einkaufspreis, dem Gewicht und der Größe des Artikels, einer möglichen Mitgliedschaft der Plattform, einer direkten Lieferung durch die Plattform oder über einen Drittanbieter (Marketplace), etc. abhängig sein können, ist es möglich, dass die von eurobuch angegebenen Versandkosten nicht mit denen der anbietenden Plattform übereinstimmen.
Detailangaben zum Buch - The Effect of Silica Nanoparticles on Hot Corrosion of Steel
EAN (ISBN-13): 9783847304579 ISBN (ISBN-10): 3847304577 Gebundene Ausgabe Taschenbuch Erscheinungsjahr: 2011 Herausgeber: Lap Lambert Academic Publishing Dez 2011
Buch in der Datenbank seit 2009-07-27T12:30:06+02:00 (Berlin) Detailseite zuletzt geändert am 2024-03-11T13:11:04+01:00 (Berlin) ISBN/EAN: 9783847304579
ISBN - alternative Schreibweisen: 3-8473-0457-7, 978-3-8473-0457-9 Alternative Schreibweisen und verwandte Suchbegriffe: Autor des Buches: padmanaban, ashwin, iyer Titel des Buches: hot steel, some like hot, silica, nanoparticles, corrosion